Vanadium |
| Simbol | V |
|---|---|
| Nama latin | Vanadium |
| Nombor Atom | 23 |
| Tempoh | 4 |
| Kategori unsor | Unsur-unsur peralihan |
| Jisim atom relatif | 50.9415 |
| Kumpulan | V.B |
| Elektronegativiti | 1.6 |
| Nombor pengoksidaan | 2, 3, 4, 5 |
| Konfigurasi elektron | 1s2 2s2 2p6 3s2 3p6 3d3 4s2 |
| Ketumpatan [g/cm3] | 6.11 |
| Keadaan | Pepejal |
| Takat lebur [°C] | 1900 |
| Takat didih [°C] | 3380 |
| Jejari atom [pm] | 171 |
| Jejari kovalen [pm] | 125 |
| Kekonduksian terma [W m-1K-1] | 30.7 |
| Muatan haba [J K-1g-1] | 0.489 |
| Discovery | 1801 |
| Kekerasan [Skala Mohs] | 6-7 |
| Kekerasan Vickers [MPa] | 628 |
| Kekerasan Brinell [MPa] | 628 |
| Modulus Young's [GPa] | 128 |
| Kekonduksian elektrik [S m-1] | 4 · 106 |
| Modulus ricih [GPa] | 47 |
| Tenaga pengionan pertama [eV] | 6.7463 |
| Tenaga pengionan kedua [eV] | 14.65 |
| Tenaga pengionan ketiga [eV] | 29.31 |
| Isotop stabil | 2 |
| Isotop tidak stabil | 5 |