Vanadium |
| Simbool | V |
|---|---|
| Latynse naam | Vanadium |
| Atoomgetal | 23 |
| Periode | 4 |
| Element kategorie | Oorgangselemente |
| Relatieve atomiese massa | 50.9415 |
| Groep | V.B |
| Electronegativiteit | 1.6 |
| Oksidering nommers | 2, 3, 4, 5 |
| Elektronkonfigurasie | 1s2 2s2 2p6 3s2 3p6 3d3 4s2 |
| Digtheid [g/cm3] | 6.11 |
| Staat | Vaste stof |
| Smeltpunt [°C] | 1900 |
| Kookpunt [°C] | 3380 |
| Atoomradius [pm] | 171 |
| Covalent radius [pm] | 125 |
| Termiese geleidingsvermoë [W m-1K-1] | 30.7 |
| Hitte kapasiteit [J K-1g-1] | 0.489 |
| Ontdekking | 1801 |
| Hardheid [Mohs-skaal] | 6-7 |
| Vickers se hardheid [MPa] | 628 |
| Brinell-hardheid [MPa] | 628 |
| Young's modulus [GPa] | 128 |
| Elektriese geleiding [S m-1] | 4 · 106 |
| Shear modulus [GPa] | 47 |
| 1ste ionisasie-energie [eV] | 6.7463 |
| 2de ionisasie-energie [eV] | 14.65 |
| 3de ionisasie-energie [eV] | 29.31 |
| Stabiele isotope | 2 |
| Onstabiele isotope | 5 |